The effect of different aging protocols on the flexural strength and phase transformations of two monolithic zirconia ceramics.

INTRODUCTION: The aim of the present study was to investigate how different aging protocols can affect the flexural strength and phase transformations of yttrium-stabilized zirconia ceramics (Y-TZP) for monolithic restorations. MATERIALS AND METHODS: Bar-shaped specimens from two zirconia ceramics bars were divided into three groups: a. no treatment (c), b. aging in an autoclave (a), and c. thermal cycling (t). The flexural strength was determined by the 3-point bending test and statistical analysis was performed to determine significant differences (p< 0.05). Weibull statistics was used to analyze the dispersion of strength values while surface microstructural analysis was performed through X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). RESULTS: Aging did not significantly affect the flexural strength but differences were recorded between the two groups, with group A presenting higher strength values and m-phase percentages. CONCLUSIONS: The observed differences between the two ceramics could be attributed to variations in composition and processing.

Aging of 3Y-TZP dental zirconia and yttrium depletion.

OBJECTIVE: Yttrium-stabilized zirconia is susceptible to low temperature degradation after interaction with water. Various mechanisms by which water molecules destabilize the tetragonal phase have been proposed, while the concept of yttrium depletion by the incorporation of hydroxyl ions in the crystalline structure either through the formation of YOH/ZrOH bonds or small α-Y(OH)3 crystallites, is prevailing. The present study was performed to investigate the surface alterations on a 3Y-TZP dental ceramic during the process of in-vitro aging and to further explore the yttrium depletion mechanism that occurs upon interaction with water. METHODS: Surface structural changes of zirconia specimens where investigated before and after in-vitro aging with X-ray diffraction analysis, Fourier-transformed infrared spectroscopy, X-ray photoelectron spectroscopy, fluorescence microscopy and scanning electron microscopy. RESULTS: High luminescence generated from the non-aged specimen was explained by the high amount of oxygen vacancies. The phase transformation from the t-ZrO2 to the m-ZrO2 phase after aging was accompanied by a significant loss of yttrium, a clear decrease of oxygen vacancies and a profound decrease of luminescence. Surface oxygen vacancies either migrated into the inner of the specimens or/and/engaged oxygen from the ZrO2 and formed the metallic phase of Y2O3 on the surface after aging. SIGNIFICANCE: An "ideal" amount of oxygen vacancies that could stabilize the tetragonal phase in Y-TZP zirconia ceramics, without compromising esthetics and LTD resistance, is still a matter of further research and different susceptibilities to LTD among various dental zirconia ceramics are based on the amount of oxygen vacancies that can be annihilated by water molecules.

Bioactivity characterization of 45S5 bioglass using TL, OSL and EPR: Comparison with the case of 58S sol-gel bioactive glass.

The current work exploits the effective application of thermoluminescence (TL), optically stimulated luminescence (OSL) and the possibility of applying Electron Paramagnetic Resonance (EPR) for the discrimination between different bioactive responses in the case of the 45S5 bioactive glass (SiO2 45, Na2O 24.5, CaO 24.5, P2O5 6 in wt%), which was synthesized through melting process. These techniques are suggested mainly due to their low spectroscopic detection thresholds. The original 45S5 in grain size range of 20-40µm was immersed in the Simulated Body Fluid (SBF) for various different immersion times ranging over one week. In this work the 110°C TL peak, a specific OSL component and the EPR signal at g=2.013 ascribed to oxygen hole center (OHC) are used due to their sensitivity to the different bioactive responses. For all luminescence and EPR components, the intensity plot versus immersion time yields sharp discontinuities, resulting in effective probes regarding the timescale for both the beginning as well as the end of the procedure of the crystalline HCAp formation respectively. On the contrary to the smooth decreasing pattern of both luminescence entities, the peak to peak amplitude of the EPR signal indicates an initial increase for the initial 16min of immersion, followed by a further decrease throughout the immersion time duration. The discontinuities monitored for both sensitivity of TL, OSL and EPR, in conjunction with the discontinuities monitored for the sensitization of TL and OSL, when plotted versus immersion time, provide an individual time scale for each one of the chemical reactions involved in the five steps of the aforementioned procedure. According to the authors' best knowledge, scarce characterization techniques could provide this time scale frame, while it is the first time that such an application of OSL and EPR is attempted. Finally, the bioactive response of the 45S5 bioglass was compared with that of the 58S sol-gel bioactive glass, in terms of the timescale of these five stages required for the final formation of the HCAp. The techniques of luminescence and EPR which take advantage of trapped charges are proposed as alternative cheap and prompt effective techniques towards discrimination between different bioactive responses in bioactive glasses.

Mechanical properties, electrochemical corrosion and in-vitro bioactivity of yttria stabilized zirconia reinforced hydroxyapatite coatings prepared by gas tunnel type plasma spraying.

Yttria stabilized zirconia reinforced hydroxyapatite coatings were deposited by a gas tunnel type plasma spray torch under optimum spraying conditions. For this purpose, 10, 20 and 30 wt% of yttria stabilized zirconia (YSZ) powders were premixed individually with hydroxyapatite (HA) powder and were used as the feedstocks for the coatings. The effect of YSZ reinforcement on the phase formation and mechanical properties of the coatings such as hardness, adhesive strength and sliding wear rates was examined. The results showed that the reinforcement of YSZ in HA could significantly enhance the hardness and adhesive strength of the coatings. The potentiodynamic polarization and impedance measurements showed that the reinforced coatings exhibited superior corrosion resistance compared to the HA coating in SBF solution. Further the results of the bioactivity test conducted by immersion of coatings in SBF showed that after 10 days of immersion of the obtained coatings with all the above compositions commonly exhibited the onset of bioactive apatite formation except for HA+10%YSZ coating. The cytocompatibility was investigated by culturing the green fluorescent protein (GFP)-labeled marrow stromal cells (MSCs) on the coating surface. The cell culture results revealed that the reinforced coatings have superior cell growth than the pure HA coatings.

Combined FTIR and SEM-EDS study of Bi2O3 doped ZnO-SnO2 ceramics.

The effects of Bi(2)O(3) addition on the phase composition, microstructure and optical properties of ZnO-SnO(2) ceramics were investigated. Starting powders of ZnO and SnO(2) were mixed in the molar ratio 2:1. After adding Bi(2)O(3) (1.0 mol.%) this mixture was mechanically activated for 10 min in a planetary ball mill, uniaxially pressed and sintered at 1300 degrees C for 2 h. Far-infrared reflection spectra were measured (100-1000 cm(-1)). To investigate the occurred differences in FTIR spectra, the Bi(2)O(3)-doped sample was examined more carefully with a Perkin-Elmer FTIR spectrometer (Perkin Elmer, Waltham, MA, USA) connected with a Perkin-Elmer FTIR microscope and itemized points of interest were also studied with SEM-EDS.

Infrared and Raman vibrational spectroscopies reveal the palette of frescos found in the medieval monastery of Karaach Teke.

Vibrational spectroscopy is applied on samples obtained from the excavation area of the medieval Monastery (10th century) of Karaach-Teke in Bulgaria. The results of the corresponding study, reveal the type of materials used for the creation of the wall-paintings and give evidence of Byzantine influence, a fact that further supports the well known impact of Byzantium on the technology and thematic-aesthetic features of iconography in Bulgaria during this era. In addition, the complementarity of FTIR and micro-Raman spectroscopies in the identification of pigments is indicated.